Effect of cyclic loading on fracture strength and microleakage of a quartz fiber dowel with different adhesive, cement and resin core material combin…
2010
Background: This study evaluated the performance of different adhesive-cement-core combinations coupled with quartz fiber dowels after cyclic loading and fracture strength tests and assessed the microleakage using dye penetration method. Methods: Forty maxillary canines (n=10 per group) were restored with fiber dowels (Quartz fiber DT Light Post) and four adhesive-cement-core material combinations [(Group 1: All-Bond 2+C&B (root) / All-Bond 2+Biscore (core); Group 2: All-Bond 2+Bisfil 2B (root) / All-Bond 2+Bisfil 2B (core); Group 3: Scotchbond 1+RelyX ARC (root) / Scotchbond 1+Supreme (core); Group 4: RelyX Unicem (root) / Scotchbond 1+Filtek Supreme (core)]. The specimens were initially c…
In vitro comparison of the retention capacity of new aesthetic brackets.
1999
Tensile bond strength and bond failure location were evaluated in vitro for two types of aesthetic brackets (non-silanated ceramic, polycarbonate) and one stainless steel bracket, using bovine teeth as the substrate and diacrylate resin as the adhesive. The results show that metallic bracket had the highest bond strength (13.21 N) followed by the new plastic bracket (12.01 N), which does not require the use of a primer. The non-silanated ceramic bracket produced the lowest bond strength (8.88 N). Bond failures occurred mainly between bracket and cement, although a small percentage occurred between the enamel-cement interface with the metal and plastic brackets and within the cement for the …
Biodegradable hydrogels obtained by photocrosslinking of dextran and polyaspartamide derivatives
2003
The functionalization of dextran with glycidyl methacrylate (GMA) leads to the formation of a derivative that generates hydrogels for irradiation at 365nm. The effects of various polymer concentrations and irradiation times on the yield and the properties of the obtained hydrogels are reported. The networks have been characterized by FT-IR spectra, dimensional analysis and swelling measurements carried out at different pH values. In vitro studies suggest that all samples undergo a partial chemical hydrolysis, whereas the incubation with dextranases causes a total degradation whose rate depends on the degree of crosslinking. In addition, aqueous solutions of functionalized dextran have been …
Reduction of Polymerization Shrinkage Stress and Marginal Microleakage Using Soft-Start Polymerization
2003
Purpose: This study evaluated the influence of a soft-start light-curing exposure on polymerization shrinkage stress and marginal integrity of adhesive restorations. Materials and Methods: Six resin-based composites (Pertac II, Tetric Ceram, Definite, Surefil, Solitaire, and Visio-Molar) were adhesively bonded to a cylindrical cavity (n = 9 per material/light) in a photoelastic material. Visible light-curing was applied using either the standard polymerization mode (800 mW/cm2 exposure duration 40 s) of the curing light (Elipar TriLight, 3M ESPE) or the exponential mode from the same device (ramp-curing: 150 mW/cm2 to 800 mW/cm2 within the first 15 s of a total curing time of 40 s). Polymer…
Cariostatic effect of a light-cured, resin-reinforced glass-ionomer for bonding orthodontic brackets in vivo
1998
The aim of this study was to evaluate in vivo the cariostatic potential of the resin-reinforced glass-ionomer (Vitremer core build-up restorative; 3M Dental Product Division) when used as a bonding agent for orthodontic brackets. The mineral distribution and topography of the enamel surface adjacent to the bracket base was determined by quantitative microradiography (TMR) and confocal laser scanning microscopy (CLSM). The study was designed in split-mouth technique using 9 pairs of premolars to be extracted for orthodontic reasons. One tooth of each pair was bonded with the resin-reinforced glass-ionomer, and the control contralateral premolar with the non-fluoridated composite (Concise, 3M…
Photoactive Yellow Protein Chromophore Photoisomerizes around a Single Bond if the Double Bond Is Locked
2020
Photoactivation in the Photoactive Yellow Protein, a bacterial blue light photoreceptor, proceeds via photo-isomerization of the double C=C bond in the covalently attached chromophore. Quantum chemistry calculations, however, have suggested that in addition to double bond photo-isomerization, the isolated chromophore and many of its analogues, can isomerize around a single C-C bond as well. Whereas double bond photo-isomerization has been observed with x-ray crystallography, experimental evidence for single bond photo-isomerization is currently lacking. Therefore, we have synthesized a chromophore analogue, in which the formal double bond is covalently locked in a cyclopentenone ring and ca…